Products

X14CrMoS17 - Nr.1.4104

Martensitic steel with low temperability. The addition of sulfur makes this type widely used for mechanical machining with chip removal, also without the quenching and tempering treatment. The resistance to corrosion is limited due to the presence of sulfur, but is better in any case with respect to the 416 type thanks to the addition of molybdenum.

References and Comparable Standards

Standard Reference: EN 10088-3: 2014 (Hot-rolled and bright products)

EUROPE		ITALY	GERMANY		FRANCE	UK	USA
EN 10088-3: 2005		(UNI 6900: 71)	(DIN 17440 - 85)		(NF A 35-574-90)	(BS 970 pt. 3-91)	AISI
Grade	N°		Werkstoff	N°
X14CrMoS17	1.4104	X10CrS17	X14CrMoS17	1.4104	Z44C14	Z13CF17	430F

Chemical Composition (Cast Analysis) (%)

C	Si / max	Mn / max	P / max	S	Mo
0,10÷0,17	1,00	1,50	0,040	15,5÷17,5	0,20÷0,60

Mechanical Properties – Rough turned (1X) in the annealed condition

Size (mm)	Heat treatment	Hardness HB max*	Rp 0,2 (MPa) min	Rm (MPa)	A5 (%) min
d≤100	Annealed (+A)	220	-	730 max	-
d≤60	Quenched + Tempered (+QT 650)	-	500	650÷850	12
60<d≤100	Quenched + Tempered (+QT 650)	-	500	650÷850	10

* only for guidance

Mechanical Properties – Cold drawn (2H, 2B) and ground bars (2G) in the solution annealed condition

Size (mm)	Annealed		Quenched + Tempered
Size (mm)	Rm (MPa) max	HB max*	Heat treatment	Rp 0,2 (MPa) min	Rm (MPa) max	A5 (%) min**	KV (J) min
d≤10	950	305	Quenched + Tempered (+QT 650)	700	900÷1150	7	-
10<d≤16	950	305		700	900÷1150	7	-
16<d≤40	900	280		650	850÷1100	8	12
40<d≤63	840	260		650	850÷1000	8	12
63<d≤100	800	245		650	850÷1000	10	12