X3CrNiMoN27-5-2 - Nr.1.4460

A duplex steel, it has a high resistance to corrosion and is widely used in particularly aggressive environments such as those of offshore platforms. With high percentages of alloy elements, it has a higher chromium content and lower molybdenum content than AISI 2205. It is widely used in Northern Europe.

References and Comparable Standards

Standard Reference: EN 10088-3: 2014 (Hot-rolled and bright products)

EUROPE		ITALY	GERMANY		FRANCE	UK	USA
EN 10088-3: 2005		-	-		(NF A 35-574-90)	(BS 1501 pt.3 -90)	AISI
Grade	N°		Werkstoff	N°
X3CrNiMoN27-5-2	1.4460	-	-	-	Z5 CND 27 - 05 AZ	-	(329)

Chemical Composition (Cast Analysis) (%)

C / max	Si / max	Mn / max	P / max	S / max	N	Cr	Mo	Ni
0,05	1,00	2,00	0,035	0,030	0,05÷0,20	25,0÷28,0	1,30÷2,00	4,5÷6,5

Mechanical Properties - Rough Turned (1X) In The Annealed Condition

Size (mm)	Hardness HB max* **	Rp 0,2 (MPa) min	Rm (MPa)**	A5 (%) min**	KV (J) min	Resistance to intergranular corrosion
Size (mm)	Hardness HB max* **	Rp 0,2 (MPa) min	Rm (MPa)**	A5 (%) min**	KV (J) min	in the delivery condition	in the welded condition
d≤100	260	450	620÷880	20	85	YES	YES

* Only for guidance
** The maximum HB values may be raised by 100HB or the tensile strenght value may be raised by 200 MPa and the minimum A% value may be lowered to 20% for bars of ≤35 mm

Mechanical Properties - Cold Drawn (2H, 2B) And Ground Bars (2G) In The Solution Annealed Condition

Size (mm)	Rp 0,2 (MPa) min	Rm (MPa)0	A5 (%) min*	KV (J) min
d≤10	610	770÷1030	12	-
10<d≤16	560	770÷1030	12	-
16<d≤40	460	620÷950	15	85
40<d≤63	460	620÷950	15	85
63<d≤100	460	620÷880	20	85

* Values valid only for size ≥5 mm

Working Temperatures Recommended

Operation	°C
Hot forgings deformation	950÷1200
Solution annealing (water, air)	1020÷1100