C10C - Nr.1.0214
Low carbon steel with a chemical composition specially designed for cold deformation. The pieces obtained are generally subjected to carburization and tempering.
References and Comparable Standards
Standard Reference: EN 10263-2: 2017
| EUROPE |
ITALY |
GERMANY |
FRANCE |
UK |
USA |
| EN 10263-2: 2001 |
(UNI 7356 - 74) |
(DIN 1654-2:89) |
(NFA35-564:83) |
- |
ASTM |
| Grade |
N° |
|
Werkstoff |
N° |
|
|
|
| (C10C) |
(1.0214) |
CB10FF |
QSt36-3 |
1.0214 |
XC10FF |
- |
- |
Chemical Composition (Cast Analysis) (%)
| C |
Si/max |
Mn |
P/max |
S/max |
Al |
| 0,08÷0,12 |
0,10 |
0,30÷0,50 |
0,025 |
0,025 |
0,020÷0,060 |
Mechanical Properties
Size
(mm) |
Untreadted (+U) or Untreadted + Peeled (+U +PE) |
Spheroidized (+AC) or as Treated + Peeled (+AC +PE) |
Cold Drawn (+U +C) |
Cold Drawn + Spheroidized + Skin Passed (+U +C +AC + LC) |
Spheroidized + Cold Drawn (+AC +C) |
| Rm (MPa) max |
Z (%) min |
Rm (MPa) max |
Z (%) min |
Rm (MPa) max |
Z (%) min |
Rm (MPa) max |
Z (%) min |
Rm (MPa) max |
Z (%) min |
| 2≤d≤5 |
- |
- |
- |
- |
- |
- |
410 |
68 |
- |
- |
| 5<d≤10 |
430 |
60 |
380 |
70 |
520 |
58 |
400 |
68 |
470 |
63 |
| 10<d≤40 |
430 |
60 |
380 |
70 |
510 |
58 |
400 |
68 |
460 |
63 |
| 40<d≤100 |
430 |
60 |
380 |
70 |
- |
- |
- |
- |
- |
- |
Working Temperatures Recommended
| Operation |
°C |
| Hot forgings deformation |
850÷1100 |
| Soft annealing |
650÷700 |